| Place of Origin: | China |
| Brand Name: | SR or OEM |
| Certification: | SGS, BV |
| Model Number: | 3105 aluminum sheet |
| Minimum Order Quantity: | Negotiable |
|---|---|
| Price: | Negotiable |
| Packaging Details: | Ocean Safe Package, Wooden Pallets/ Cases |
| Delivery Time: | 5 - 30 days |
| Payment Terms: | T/T, L/C, Western Union |
| Supply Ability: | 1000 tons per month |
| Alloy: | 3105 | Color: | Natural Color Or RAL |
|---|---|---|---|
| Surface: | Mill Finish/coated | Application: | Architectural Decoration |
| Thickness: | 0.2-6mm | Temper: | O H |
| Width: | 200-2600mm | Length: | 500-12000mm |
| High Light: | high strength aluminum sheet,alloy aluminum sheet |
||
ASTM EN JIS 3105 Good Mechanical Properties aluminum sheet for architectural decoration
3105 aluminum coil with 98% pure aluminum and slight alloy additions for strength. 0.3% of copper is added to 3105 aluminum coil, so the conductivity turns out to be 41%. For its contents and processing technologies, 3105 aluminum coil is light in weight and it has semi-smooth surface. Besides, it is not hardened by heat treatment.
Application:
Mg, Mn and Si are added to 3105 aluminum coil, thus, it has excellent correction resistance, formability and welding characteristics. Besides, it has average mechinability and it can be increased in harder tempers than in annealed condition. Oil lubricants should be used for all machining operations. The forming characteristics of 3105 aluminum coil are pretty good by all conventional processes regardless of temper. But 3105 aluminium coil does not respond to heat treatment except for annealing during cold working. The cold working characteristics are very good, even in the harder cold working tempers. For all the features above, 3105 aluminum coil has a vast application in many field.
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 2.6-2.8 | 25 | |
| Poisson's Ratio | 0.33 | 25 | |
| Elastic Modulus (GPa) | 70-80 | 25 | |
| Tensile Strength (Mpa) | 150 | 25 | H12 |
| Yield Strength (Mpa) | 130 | ||
| Elongation (%) | 7 | ||
| Reduction in Area (%) | |||
| Shear Strength (MPa) | 97 | 25 | H12 |
Thermal Properties
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Thermal Conductivity (W/m-K) | 173 | 25 | O (all) |